To render polymeric materials osteoinductive, nano-sized calcium phosphate apatite particles (CaP) were introduced into a low molecular weight poly(D,L-lactide). Homogenous composites were made with 10%, 20% and 40% by weight of apatite content while pure polylactide was used as control. Thereafter porous samples (pore size 300-400 µm, 60% porosity) were fabricated and sterilized.In vitrostudies showed that calcium ions were released from the composites depending on the apatite content, while surface mineral deposition was observed only on the 40% CaP composites in simulated body fluid (SBF) within 14 days. After 12 weeks of intramuscular implantation in dogs, only the 40% CaP composite implant retained its shape and showed ectopic bone formation within the pores. In conclusion, adding a content of 40% apatite into poly(D,L-lactide) could lead to an osteoinductive material. Future studies will focus on understanding this phenomenon of material-directed osteoinduction in order to develop a promising bone graft substitute.