Hydrogels pose interesting features for cartilage regeneration strategies, such as the option for injectability andin situgelation resulting in optimal filling of defects. We aimed to study different hydrogels for their capability to support chondrogenesis of human bone marrow-derived mesenchymal stem cells (hBMSCs). hBMSCs were encapsulated in alginate, alginate with hyaluronic acid (alginate/HA), fibrin or thermoresponsive HA grafted with poly(N-isopropyl acrylamide) side-chains (HA-pNIPAM). Glycosaminoglycan production and cartilage-related gene expression were significantly higher in hBMSC-alginate and hBMSC-fibrin constructs than in the other constructs. Supplementation of alginate with HA was not beneficial. hBMSC-alginate, hBMSC-fibrin and hBMSC-HA-pNIPAM constructs were placed in simulated defects in osteochondral biopsies and culturedin vitrofor 28 d. Biopsies containing hBMSC-alginate and hBMSC-fibrin were implanted subcutaneously in nude mice for 12 weeks. hBMSC-alginate constructs had significantly higher cartilage-related gene expression after 28 d of culture as well as significantly more safranin-O positive repair tissue after 12 weeksin vivothan hBMSC-fibrin constructs. Although initial experiments with hBMSC-hydrogel constructs suggested comparable results of hBMSC-alginate, hBMSC-fibrin and hBMSC-HA-pNIPAM constructs, culture in the osteochondral biopsy modelin vitroas well asin vivorevealed differences, suggests that chondrogenesis of hBMSCs in an osteochondral environment is hydrogel-dependent.